Nestled in the heart of Safat, Kuwait, Nimish Metal has built a reputation for reliability and expertise in the industrial supply sector. We understand that your projects demand the highest quality materials, which is why we take pride in providing premium Tool and Die Steel H13 bars. Sourced from trusted mills, our H13 steel is the backbone of durability for demanding applications, ensuring that your tools and dies can withstand intense heat and pressure, project after project, delivering consistent and exceptional results.
The strength of H13 steel lies in its sophisticated composition, primarily a balance of chromium, molybdenum, and vanadium. This specific blend gives the steel its remarkable ability to retain hardness and resist wear even when exposed to high temperatures. After proper heat treatment, H13 bars achieve excellent toughness, meaning they can handle significant impact without cracking. This combination of hot hardness and mechanical strength is what makes it a preferred choice for the most challenging industrial environments.
| ASTM A681 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| H13 | 0.32 | 0.45 | 0.2 | 0.6 | 0.03 | 0.03 | 0.8 | 1.25 | 4.75 | 5.5 | 0.8 | 1.2 | 1.1 | 1.75 |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| 1.2344 /X40CrMoV5-1 | 0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.85 | 1.15 | 1.1 | 1.5 |
| JIS G4404 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| SKD61 | 0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.8 | 1.15 | 1.0 | 1.5 |
| Properties | Metric | Imperial |
| Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) | 1200 – 1590 MPa | 174000 – 231000 psi |
| Tensile strength, yield (@20°C/68°F, varies with heat treatment) | 1000 – 1380 MPa | 145000 – 200000 psi |
| Reduction of area (@20°C/68°F) | 50.00% | 50.00% |
| Modulus of elasticity (@20°C/68°F) | 215 GPa | 31200 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Country | USA | German | Japan |
| Standard | ASTM A681 | DIN EN ISO 4957 | JIS G4404 |
| Grades | H13 | 1.2344/X40CrMoV5-1 | SKD61 |
| Properties | Conditions | ||
|---|---|---|---|
| T (ºC) | Treatment | ||
| Thermal expansion | 10.4 x 10-6/ºC | 20-100 | – |
| Thermal conductivity | 28.6 W/mK | 215 | – |
When choosing Tool and Die Steel H13 bars, consider factors such as hardness, heat resistance, wear resistance, toughness, machinability, and the specific requirements of the application, including temperature and load conditions.
Tool and Die Steel H13 bars offer limited corrosion resistance due to their high alloy content, but they can still be susceptible to rusting in harsh environments. To improve corrosion resistance, they may require additional surface treatments like coating or regular maintenance to prevent degradation.
When it comes to application, H13 bars from Nimish Metal are incredibly versatile. They are the go-to material for creating high-performance die-casting dies, forging dies, and extrusion presses that operate under extreme thermal cycling. You’ll also find them perfectly suited for mandrels, hot work punches, and plastic injection molds. Essentially, any tooling that must perform reliably while being repeatedly heated and cooled is an ideal candidate for the robust performance offered by H13 steel, making it a fundamental component in modern manufacturing.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Nimish Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Safat, Kuwait
Copyright 2024 Nimish Metals. All rights reserved