Nestled in the industrial heart of Safat, Kuwait, Nimish Metal has established itself as a trusted name for top-tier stainless steel solutions. We are proud to present our high-quality Stainless Steel 1.4122 bars, a martensitic grade specifically engineered for demanding environments. This material is particularly valued for its exceptional hardness and superior resistance to corrosion, making it a reliable choice for engineers and fabricators who cannot compromise on performance or durability in their critical projects.
The strength of 1.4122 stainless steel comes from its carefully balanced composition, which includes chromium for corrosion resistance and a higher carbon content that allows it to achieve impressive hardness through heat treatment. This creates a bar stock that is not only tough and wear-resistant but also retains good mechanical properties under stress. It’s this robust combination that provides the structural integrity needed for parts that must withstand significant abrasion and pressure without faltering.
Length : 1 To 6 Meters, Custom Cut Length
Round bar : Diameter: 3mm~ 800mm
Angle bar : Size: 3mm* 20mm* 20mm~ 12mm* 100mm* 100mm
Square bar : Size: 4mm* 4mm ~100mm* 100mm
Flat bar : Thickness: 2mm ~ 100mm / Width: 10mm ~ 500mm
Hex bar : Size: 2mm ~ 100mm
Form : Round, Square, Hex(A/F), Rectangle, Billet, Ingot, Forging Etc
Surface Finishing : Pickled, Black, Bright, Polishing, Blasting, etc
Test Reports : SGS, BV, API, BSI, GHC.
Packing : Each steel bar has the singal, and several will be bundled by weaving bag or as per requirement.
Specials : Sizes and Specifications other than above can be manufactured on request
| Grade | C | Si | Mn | P | S | Cr | Mo | N | Others |
| SS 1.4122 | 0.33-0.45 | max 1.00 | max 1.5 | max 0.040 | max 0.015 | 15.5-17.5 | 0.80-1.30 | max 1.00 | – |
| Yield Rp0.2 (MPa) | Tensile Rm (MPa) | Impact KV/Ku (J) | Elongation A (%) | Reduction in cross section on fracture Z (%) | As-Heat-Treated Condition | Brinell hardness (HBW) |
| 869 (≥) | 926 (≥) | 41 | 44 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 |
| EN | DIN | AFNOR |
| 1.4122 | 1.4122 – X 39 Cr Mo 17 1 | Z 38 CD 16-01 |
Yes, Stainless Steel 1.4122 bars can be recycled after use. Stainless steel is highly recyclable, retaining its properties and reducing environmental impact, making it a sustainable material for reuse.
Yes, Stainless Steel 1.4122 bars can be welded. It is weldable using standard methods like TIG or MIG welding, though pre-heating and post-weld heat treatment may be required for optimal results.
Yes, Stainless Steel 1.4122 bars can be heat treated. It can be hardened through quenching and tempering processes, improving strength and wear resistance while maintaining its corrosion resistance properties.
Thanks to its unique properties, our 1.4122 bars are the preferred material for components that face harsh conditions daily. You will commonly find them used in the manufacture of precision shafts, pump components, and valve parts within the oil and gas industry. Beyond that, they are essential for crafting durable surgical and dental instruments, cutting tools, and high-wear industrial parts, proving their versatility and reliability across medical, manufacturing, and marine applications where failure is not an option.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Nimish Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Safat, Kuwait